Ultradur® S 4090 G2
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aaTT8v_Ultradur-S-4090-G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low-warpage, easy-flowing injection molding grade with 10 % glass fibres for technical parts, for which dimensional stability is very important (eg, housings, plug-and-socket connectors). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 35.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 105 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 0.46 | % | |
| free, transverse | 0.85 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 170 | °C | |
| Temperature Index - at 50% loss of tensile strength | IEC 60216 | ||
| -- 3 | 110 | °C | |
| -- 4 | 140 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | < 250 | mm/sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2 |
| Tensile Creep Modulus 5(1000 hr) | 3300 | MPa | ISO 899-1 |
| Flexural Modulus | 4100 | MPa | ISO 178 |
| Flexural Stress | 119 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 24 | kJ/m² | |
| 23°C | 37 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1200 | J/kg/°C | |
| Thermal Conductivity | 0.27 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.1E-3 | ||
| 1 MHz | 0.021 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 375 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Processing (Melt) Temp | 250 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| 3 . | 20000 h |
| 4 . | 5000 h |
| 5 . | strain <= 0,5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 140 Z L | RTP Company | PP Homopolymer | RTP |
| NuSil FS1-3730 | NuSil Technology | Silicone | NuSil |
| ASTAMID™ KB3EG5 | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |
| KumhoSunny ABS HU650Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| POLYfill PPH TS15030 | Polykemi AB | PP Homopolymer | POLYfill |