GETILAN GPE/200 E
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aZwLpV_GETILAN-GPE-200-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN: is our trade-mark of our crosslinkable polythene. GETILAN GPE/200 E: medium density chemically crosslinkable compound for low and medium voltage power cable insulation and sheathing. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our type MAC/100 PSF or MAC/100 SCU (red cupper resistant). REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 Certify: BS 7655 GP8,IEC502 XLPE |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 - 0.70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 15.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 400 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | 8.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | -10 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 200°C | 40 | % | IEC 60811 |
| Residual Value | -5.0 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor- 50 Hz (23°C) | 4.00E-4 | IEC 250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 215 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | BS 6622 |
| Dielectric Strength (20°C) | 21 | kV/mm | IEC 243 |
| Relative Permittivity (23°C) | 2.36 | IEC 250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 145 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Die Temperature | 220 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90 °C for two hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Note Message | |
|---|---|
| 1 . | 20 N/cm2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® E185SB | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| APEX® 78-A447H-3 | Teknor Apex Company | PVC, Flexible | APEX® |
| Huafon JF-W-D6070 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Pearlbond™ 123 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| Sylvin 2990-78 Clear Green 3197 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |