Order Products : sales@su-jiao.com
SABIC® HDPE M453SE
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aZFIIl_SABIC-HDPE-M453SE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE M453SE is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties. Typical applications. SABIC® HDPE M453SE is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.0 | g/10 min | |
| 190°C/5.0 kg | 11 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 65.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 26.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 31.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1200 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 5.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 81.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 124 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Enthalpy Change | 203 | J/g | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Pressure | 93.0 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MonoSol® M7061 | MonoSol, LLC | PVOH | MonoSol® |
| Vibrathane® 6020U | Chemtura | PUR-Ester/MDI | Vibrathane® |
| Arak LLDPE HD5218EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Capa™ 6500C | Perstorp Holding AB | PCL | Capa™ |
| Hostacom TYC 727N E C12716 | LyondellBasell Industries | PP Copolymer | Hostacom |