SNOLEN® EC 4/48
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aYkNHk_SNOLEN-EC-4-48.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES High impact strength. MAJOR APPLICATIONS Wire and cables isolation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.944 to 0.948 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 63 to 77 | g/10 min | |
| 190°C/5.0 kg | 3.0 to 4.0 | g/10 min | |
| Melt Flow Ratio | 16.0 to 24.0 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 24.0 | MPa | |
| Break | 32.0 | MPa | |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 77.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND POMH 100P-100RG | NEXT Specialty Resins, Inc. | Acetal (POM) Homopolymer | NEXT REGRIND |
| Complet® LGF60-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| ISORENE™ CA3-7001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| Lifoflex® GB 1040 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| TechnoElast A 8000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |