HANWHA LLDPE HS1100
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aYKOkn_HANWHA-LLDPE-HS1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE HS1100 is high strength LLDPE manufactured by Unipol process and designed for heavy-duty film. LLDPE HS1100 has excellent mechanical property, processability and heat seal property. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 850 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 190 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 190 µm | 47.1 | MPa | ASTM D882 |
| TD : Fracture, 190 µm | 43.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 190 µm | 600 | % | ASTM D882 |
| TD : Fracture, 190 µm | 800 | % | ASTM D882 |
| Dart Drop Impact (190 µm) | > 800 | g | ASTM D1709B |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 190.0 µm | 137.3 | kN/m | ASTM D1004 |
| TD : 190.0 µm | 147.1 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Peak Melting Temperature | 126 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (190 µm) | 25 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 1.5 to 2.5Optimum Gage Range: 0.10 to 0.30 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 AR 15 | RTP Company | PP, Unspecified | RTP |
| Sindustris PP HI5303RB | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Grivory® GV-4 FWA nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Karina WHITE PVC COMPOUND 710-10/1-O-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ MF002AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |