Celanex® 3200FC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aWnkQP_Celanex-3200FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3200FC is a general purpose, 15% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 26 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.10 - 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.17 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 6410 | MPa | ASTM D638 |
| 0°C | 6210 | MPa | ASTM D638 |
| 23°C | 5520 | MPa | ASTM D638 |
| 80°C | 2450 | MPa | ASTM D638 |
| 121°C | 2070 | MPa | ASTM D638 |
| -- | 5800 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 108 | MPa | ASTM D638 |
| Fracture, 0°C | 105 | MPa | ASTM D638 |
| Fracture, 23°C | 93.1 | MPa | ASTM D638 |
| Fracture, 80°C | 55.2 | MPa | ASTM D638 |
| Fracture, 121°C | 44.8 | MPa | ASTM D638 |
| Fracture | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 1.9 | % | ASTM D638 |
| Fracture, 0°C | 2.0 | % | ASTM D638 |
| Fracture, 23°C | 3.0 | % | ASTM D638 |
| Fracture, 80°C | 6.3 | % | ASTM D638 |
| Fracture, 121°C | 6.3 | % | ASTM D638 |
| Fracture | 3.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | ISO 179/1eU |
| 23°C | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 192 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 195 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 90.0 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 18 | kV/mm | ASTM D149 |
| -- | 29 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.50 | ASTM D150 | |
| 100 Hz | 4.20 | IEC 60250 | |
| 1 MHz | 3.80 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.020 | ASTM D150, IEC 60250 | |
| 100 Hz | 1.6E-3 | IEC 60250 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index | |||
| -- | 350 | V | IEC 60112 |
| -- | 250 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.710 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1002 HI UV | RTP Company | PBT | RTP |
| TEREZ PA 6.10 7500 GF 30 ECO | TER HELL PLASTIC GMBH | Nylon 610 | TEREZ PA 6.10 |
| VITAMIDE® AB76BK8529 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| DENILUB Z 00U 4TF | Vamp Tech | PPA | DENILUB |
| NORYL PPX™ PPX630 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL PPX™ |