Rotec® ASA S 210
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aVcIR3_Rotec-ASA-S-210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rotec®ASA S 210 is an acrylonitrile-styrene-acrylate (ASA) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main characteristics of ASA S 210 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 52.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 22 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity ISO 8302, was tested in accordance with DIN 52612. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 210 - 250 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 210 - 250 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Screw rotation speed: moderate to highBack pressure: low to moderateInjection pressure: tool depending |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | < 245 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6060 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| ELIX™ ABS H950 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Grilamid® L 20 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LNP™ THERMOCOMP™ ZX08309 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |
| Plenco 01508 (Transfer) | Plastics Engineering Co. | Polyester, TS | Plenco |