Order Products : sales@su-jiao.com
SAXAMID™ 126F10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aTXSL9_SAXAMID-126F10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 126F10 is a polyamide 6 injection-molding-grade reinforced with 50 % glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15400 | MPa | ISO 527-2/1 |
| Tensile Stress | 209 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11400 | MPa | ISO 178 |
| Flexural Stress 2 | 328 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 89 | kJ/m² | |
| 23°C | 90 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 82 | kJ/m² | |
| 23°C | 84 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 214 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 216 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 to 1.70 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIRASON™ 1250BK40 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| Axiall PVC 8540 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Eco-Solutions GP330-0 | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| Sylvin 83039-74 White 1493 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RONFALIN® ABS 1361 | A. Schulman Europe | ABS | RONFALIN® |