Menzolit® CarbonSMC 0400 is an developmental carbon fibre low profile SMC for automotive applications. It fulfils the requirements of the automotive industry regarding painted body panels including low C-emissions. For highest surface quality we recommend processing on mirror finished chrome-plated steel moulds. The product's thermal resistance allows for on-line painting at 190- 200°C. Adhesion of paint or IMC is excellent. The material doesn't shrink during moulding, it even expands. Therefore warpage is reduced and dimensional stability is excellent.

General Information
Filler / Reinforcement	Mineral filler Carbon fiber reinforced material
Features	Good dimensional stability Low warpage Low smoke Sprayable Good adhesion Low shrinkage Halogen-free
Uses	Application in Automobile Field
Forms	Particle
Processing Method	Compression molding
Part Marking Code (ISO 11469)	>UP-(CF+MD)60

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm³	ISO 1183
Molding Shrinkage	-0.17	%	ISO 294-4
Water Absorption (Saturation, 23°C)	0.50	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	32.0	MPa	ISO 527-2
Tensile Stress (Yield, Compression Molded)	138	MPa	ISO 527-2
Tensile Strain (Break, Compression Molded)	1.4	%	ISO 527-2
Flexural Modulus (Compression Molded)	28000	MPa	ISO 178
Flexural Stress (Compression Molded)	324	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Compression Molded)	57	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	185	°C	DSC
CLTE - Flow	8.0E-6	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (2.00 mm)	HB		UL 94

Additional Information
Fibre Content UD, total, EN ISO 1172: % 60Post Moulding Shrinkage DIN 53464: 0 %Heat Distortion Temp. EN ISO 75-2: >200°CContinous Service Temp. Menzolit method: 180 °CPoison's Ratio Menzolit method: 0,30Tensile Rupture Strain EN ISO 527-4: 1.40%Matrix Crazing Strain Menzolite method: 0.40%Compression Strength EN ISO 14126: 140 MPaThe value listed as Molding Shrinkage, ISO294-4, was tested in accordance with ISO 2577.The values listed as Flexural Strength and Flexural Modulus ISO 178, were tested in accordance with ED ISO 14125.

Additional Information

Fibre Content UD, total, EN ISO 1172: % 60Post Moulding Shrinkage DIN 53464: 0 %Heat Distortion Temp. EN ISO 75-2: >200°CContinous Service Temp. Menzolit method: 180 °CPoison's Ratio Menzolit method: 0,30Tensile Rupture Strain EN ISO 527-4: 1.40%Matrix Crazing Strain Menzolite method: 0.40%Compression Strength EN ISO 14126: 140 MPaThe value listed as Molding Shrinkage, ISO294-4, was tested in accordance with ISO 2577.The values listed as Flexural Strength and Flexural Modulus ISO 178, were tested in accordance with ED ISO 14125.

Injection	Nominal Value	Unit
Mold Temperature	155 - 160	°C
Injection Pressure	5.00 - 12.0	MPa

Resin Grade	Manufacturer	Category	Trademark
Stirol UPS-1002 L	JSC CONCERN STIROL	PS (HIPS)	Stirol
TOTAL Polypropylene PPC 5571	TOTAL Refining & Chemicals	PP Impact Copolymer	TOTAL Polypropylene
Adell PP EL-37	Adell Plastics, Inc.	PP Homopolymer	Adell PP
Elastollan® 685 A	BASF Polyurethanes GmbH	TPU-Polyester	Elastollan®
LUVOCOM® 1/CF/20-OS	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®

Category:	Polyester, TS , Thermoset Polyester
Manufacturer:	Menzolit Ltd (UK)
Trademark:	Menzolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aTQV2b_Menzolit-CarbonSMC-0400.pdf
PRICE:	Order Products email sales@su-jiao.com