Ravago Compounds PP-4342
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Ravago Compounds |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aSix7I_Ravago-Compounds-PP-4342.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Key Features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - Tangent (23°C) | 2600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 124 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.52 mm | HB | UL 94 | |
| 3.05 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 93.3 | °C | |
| Drying Time | 0.0 - 8.0 | hr | |
| Rear Temperature | 193 - 238 | °C | |
| Middle Temperature | 193 - 238 | °C | |
| Front Temperature | 193 - 238 | °C | |
| Nozzle Temperature | 193 - 238 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Injection instructions |
|---|
| Hot Runner Temperature (if applicable): 420 to 450°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP510-01UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| TRISTAR® PC-10R-(22) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Viton® VTR-9217 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| BIOLLOY KG340 | Techno Polymer Co, Ltd. | PLA+ABS | BIOLLOY |
| POLIMAXX 1100RC | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |