| 30% glass fiber reinforced, impact modified Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.27 | -- | g/cm³ | ISO 1183/A |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 195 | 135 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8600 | 5600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 150 | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.5 | 5.5 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | -- | kJ/m² | |
| 23°C | 20 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 80 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | > 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | > 250 | -- | °C | ISO 306/A50 |
| -- | 240 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (135°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers A3 PRTA010 70A UP321 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| K-Prene GHT 65 | Technovinyl Polymers India Ltd. | TPE | K-Prene |
| Karina LILAC COLOR CONCENTRATE -E 34/ 20-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaskon MUF-2A | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| LNP™ THERMOCOMP™ RC004SXS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |