Duron PEI 2200
| Category: | PEI , Polyether Imide |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | Duron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aRd29B_Duron-PEI-2200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duron PEI 2200 is a 20% glass filled polyetherimide that offers a superior combination of mechanical, electrical, and thermal properties. PEI is inherently flame resistant with low smoke emission. It provides outstanding processability and good chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 140 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6500 | MPa | ASTM D790 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Vicat Softening Temperature | 221 | °C | ASTM D1525 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 9 kJ/m²Unnotched Izod Impact, ASTM D256: 30 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Xuchuan XCNS 3001 C-B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Next PC CX-01BK | Next Polymers Ltd. | PC | Next PC |
| Karina PVC COMPOUND E-75853-35/1-BY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Zytel® ST811HS NC010 | DuPont Performance Polymers | Nylon 6 | Zytel® |