| Message |
|---|
| Vyncolit® X640 is a glass fiber reinforced resol resin based molding material with excellent mechanical and thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Apparent Density | 0.64 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.19 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Post Shrinkage | 0.070 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.6 | % | ISO 2577 |
| Tensile Modulus (Injection Molded) | 17000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 138 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 1.0 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 16000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 254 | MPa | ISO 178 |
| Compressive Stress | 308 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 5.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 34 | kV/mm | IEC 60243-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 25 FR | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| WPP PP PPC6CF-1-001 White | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| HiFill® TPU 0600 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |
| Jackdaw PC DX20NT6460 | Jackdaw Polymers | PC | Jackdaw PC |
| Sylvin 5170-85 Grey 9632 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |