Monprene® OM-10230-01
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aP95FG_Monprene-OM-10230-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®OM-10230-01 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Monprene®The main features of the OM-10230-01 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.6 | % | ASTM D955 |
| Transverse flow | 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 34 | ASTM D2240 | |
| Shaw A, 5 seconds | 30 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 1.72 | MPa | ASTM D412 |
| Tensile Strength (Break) | 2.76 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 500 | % | ASTM D412 |
| Compression Set (23°C, 22 hr) | 10 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 to 2.80mm, All Colors) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 188 | °C | |
| Middle Temperature | 154 - 199 | °C | |
| Front Temperature | 154 - 216 | °C | |
| Nozzle Temperature | 154 - 221 | °C | |
| Processing (Melt) Temp | 166 - 221 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 潮湿会使材料降解。建议进行干燥处理。可以把材料放入除湿干燥机，在140°F的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tisakril® ABS 15 GFR | Tisan | ABS | Tisakril® |
| Karina RED PVC COMPOUND 902-42/291-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS DE265 - 7905/3 | AD majoris | PP, Unspecified | MAJORIS |
| Axiall PVC 8266 Natural 04 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Sylvin 9067-60 Grey 9584 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |