DIAMALOY ENGINEERED ALLOYS ABS NYLON 4010A
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ENGINEERED ALLOYS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aOPciI_DIAMALOY-ENGINEERED-ALLOYS-ABS-NYLON-4010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIAMALOY ENGINEERED ALLOYS ABS NYLON 4010A is an Acrylonitrile Butadiene Styrene + Nylon (ABS+Nylon) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(265°C/5.0 kg) | 37 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 3.18 mm, Injection Molded) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C, 3.18 mm, Injection Molded | 42.2 | MPa | |
| Yield, 23°C, 3.18 mm, Injection Molded | 43.6 | MPa | |
| Break, 23°C, 3.18 mm, Injection Molded | 35.9 | MPa | |
| Break, 23°C, 3.18 mm, Injection Molded | 39.4 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 23°C, 3.18 mm, Injection Molded 3 | 3.7 | % | |
| Yield, 23°C, 3.18 mm, Injection Molded 4 | 3.6 | % | |
| Break, 23°C, 3.18 mm, Injection Molded 5 | 15 | % | |
| Break, 23°C, 3.18 mm, Injection Molded 6 | 200 | % | |
| Flexural Modulus - Tangent 7(23°C, 3.18 mm, Injection Molded, 50.8 mm Span) | 1480 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm, Injection Molded) | 52.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 8 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 232 to 260 | °C | |
| Front Temperature | 235 to 260 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | double gate |
| 4 . | single gate |
| 5 . | double gate |
| 6 . | single gate |
| 7 . | Method I (3 point load), 1.3 mm/min |
| 8 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 660.75 FR | RTP Company | ABS | RTP |
| Silopren® LSR 7005 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| GELOY™ XP4020R resin | SABIC Innovative Plastics Asia Pacific | ASA+PC | GELOY™ |
| Geon™ Vinyl Packaging XPL 293 FROST 1733 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| INNOPOL® PP CS 1-5120 LH | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |