INEOS HDPE G60-25-144
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aNuS6T_INEOS-HDPE-G60-25-144.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| G60-25-144 is a high density polyethylene homopolymer typically used in the production of sheet extrusion and blow molded containers. This material meets the Food and Drug Administration requirements of 21CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.25 | g/10 min | |
| 190°C/21.6 kg | 26 | g/10 min | |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | 20.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 31.0 | MPa | |
| Break | 31.0 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.0 | % | |
| Break | 950 | % | |
| Flexural Modulus - 2% Secant | 1360 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 450 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 44.7 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79.4 | °C | ASTM D648 |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Oxidation Induction Time (210°C) | > 15 | min | ASTM D3895 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Restramid PA 6 30GF | Polimarky Spolka Jawna | Nylon 6 | Restramid |
| Retpol® 3029 UV3 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Karina WHITE PVC COMPOUND 751D10/ 31-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® MN-3600HA | TEIJIN LIMITED | PC | Panlite® |
| 3M™ Dyneon™ Fluoroelastomer FC 1610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |