Hostacom D1171 9176
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aNN4G2_Hostacom-D1171-9176.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% talc filled copolymer,antistatic. Previously known as 2611PC TA5. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Secant | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.9 | kJ/m² | ISO 179 |
| 23°C | 8.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 55.0 | °C | ISO 306 |
| Additional Information |
|---|
| Coefficient of Linear thermal Expansion, DIN 53752, 23 - 85°C, Parallel: 0.75 1/KFlammability, FMVSS 302: 40 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 862 | RTP Company | Acetal (POM) Homopolymer | RTP |
| Sinpolene CPP2020 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | Sinpolene |
| Syncure™ S1027A | PolyOne Corporation | XLPE | Syncure™ |
| Gallonprene® GP210-3004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| REV Materials 8006-001 | REV Materials | PP, Unspecified | REV Materials |