Capilene® M 45 F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aLVmUV_Capilene-M-45-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® M 45 F is a polypropylene homopolymer intended for cast film extrusion. CAPILENE ® M 45 F features: slip and anti-blocking additives, slightly modified molecular weight distribution, high gloss, high transparency and good stiffness. CAPILENE ® M 45 F is suitable for: high quality cast films for packaging food and other items, lamination films, water-quenched blown films; blow molding and injection molding products. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 32.0 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 13 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1500 | MPa | ASTM D790 |
| -- 3 | 1350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256 |
| 23°C | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/A, ASTM D1525 4 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (40.0 µm) | 2.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 37T1020 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| Shin-Etsu RTV KE-1300T | Shin-Etsu Silicones of America | Silicone Rubber, RTV-2 | Shin-Etsu RTV |
| New-prene™ 8280N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Nipolon® -L Nipolon®-L | TOSOH Corporation | LLDPE | Nipolon® -L |
| Wanthane® WHT-1189B | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |