Geon™ Vinyl Dry Blend E1501
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Dry Blend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aLTiar_Geon-Vinyl-Dry-Blend-E1501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VSI FLAMMABILITY:Burn Length (0.040 in Bar)ASTM D635 0* IN.Burn Time (0.040 in Bar) ASTM D635 0* Sec.*Extinguished before 25 MM starting ref mark. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 16354 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2950 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 41.6 | MPa | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 0°C, 3.18 mm, Compression Molded | 85 | J/m | |
| 23°C, 3.18 mm, Compression Molded | 520 | J/m | |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 84.5 | J/cm | |
| 23°C 4 | 178 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 3.18 mm, Compression Molded) | 73.9 | °C | ASTM D648 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Procedure A, C.125 Dart |
| 4 . | Procedure B, C.125 Dart |
| 5 . | annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP491S | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| AKROTEK® PEEK TM natural (5069) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Greenflex® FD 50 | Versalis S.p.A. | EVA | Greenflex® |
| Sylvin 8977-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP420J | PolyMirae | PP Homopolymer | Moplen |