EnCom HPP CCF20 BK41000
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | EnCom, Inc. |
| Trademark: | EnCom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aKtDTL_EnCom-HPP-CCF20-BK41000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20 % Calcium Carbonate Filled HomoPolymer PP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 42.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 2.0E-3 | % | |
| Rear Temperature | 188 to 216 | °C | |
| Middle Temperature | 199 to 232 | °C | |
| Front Temperature | 199 to 232 | °C | |
| Nozzle Temperature | 193 to 227 | °C | |
| Processing (Melt) Temp | 204 to 260 | °C | |
| Mold Temperature | 18.3 to 54.4 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 5790B | Teknor Apex Company | TPV | Sarlink® TPV |
| SEPAZ™ K130HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| Armlen® PP SM 20-5UP | Poly Plastic | PP, Unspecified | Armlen® |
| Fortron® 1130L0 | Celanese Corporation | PPS | Fortron® |
| Karina NATURAL PVC COMPOUND -E 730D25/ 1-IS-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |