Pibiter® NRV20 NAT001
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiter® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aKKqdc_Pibiter-NRV20-NAT001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fiber reinforced PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption | |||
| 23°C, 24 hr | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Ash Content | 20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ASTM D638 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6400 | MPa | ASTM D790 |
| Flexural Strength | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 206 | °C | |
| Vicat Softening Temperature | 210 | °C | ASTM D1525 1 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 3.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk 60GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | PBT | Niuk |
| Dynaglide® DW 602GN | DeWAL Industries | PTFE | Dynaglide® |
| HiFill® PA4/6 GF50 HS BK | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| LubriOne™ NN-25GB/15T | PolyOne Corporation | Nylon 66 | LubriOne™ |
| KOCETAL® K100HS | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |