4MID® 9B22140 HUV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | 4Plas |
| Trademark: | 4MID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aHXHXC_4MID-9B22140-HUV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4MID 9B22140 HUV is a Prime Standard Flow 40% Glass Fibre Reinforced Heat & UV Stabilised PA6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Vertical flow direction | 0.90 | -- | % | |
| Flow direction | 0.20 | -- | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Moisture Content | < 2000 | -- | ppm | ISO 960 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 8000 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 160 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | -- | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 12 | -- | kJ/m² | ISO 180/1A |
| 23°C | 14 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 70 | -- | kJ/m² | ISO 180/1U |
| 23°C | 80 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B |
| Melting Temperature 2 | 223 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2244 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Sicoklar UG35 | Ravago Group | PC | Sicoklar |
| Nycal™ 1850L3H Bk-2 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| ALTECH® PP-B A 4430/100 MR30 | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |
| Daelim Po1y® LL-25 | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |