Formolene® 6535N
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aHW9ZR_Formolene-6535N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Impact Copolymer Designed to Meet the Requirement of Automotive Interior Trim Formolene® 6535N is a specially formulated, high impact copolymer of polypropylene designed for interior trim applications such as those described by Ford Motor Company's Specifications WSS-M4D638-A and WSS-M4D638-B. Formolene ® 6535N is suitable for many injection molding applications requiring toughness such as bins, crates, outdoor tools, machinery and toys. Material has been approved under GM-PP-033 and DCX MSB-500 for interior trim. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 80°C, 48 hr | 1.6 | % | |
| Flow : 80°C, 48 hr | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D, Injection Molded | 63 | ASTM D2240 | |
| -- | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 23.4 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield | 86 | % | ISO 527-2/50 |
| Break, Injection Molded 2 | 100 | % | ASTM D638 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded 3 | 1070 | MPa | ASTM D790 |
| -- | 1130 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 23.4 | MPa | ISO 527-3/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C, Injection Molded | 64 | J/m | ASTM D256 |
| -18°C, Injection Molded | 80 | J/m | ASTM D256 |
| 23°C, Injection Molded | 130 | J/m | ASTM D256 |
| -40°C | 5.5 | kJ/m² | ISO 180 |
| -18°C | 6.5 | kJ/m² | ISO 180 |
| 23°C | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 97.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 52.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEALID XN060 - 8229 | AD majoris | Nylon, Unspecified | NEALID |
| Borealis PP SR552 | Borealis AG | PP, Unspecified | Borealis PP |
| Foam-It® 15 | Smooth-On, Inc | PUR, Unspecified | Foam-It® |
| Kepital® TC3020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Dow Corning® C6-180 | Dow Corning Corporation | Silicone | Dow Corning® |