Starex BF-0950
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aGvL9Q_StarexBF0950.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex BF-0950 is a methyl methacrylate/ABS (MABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.35 - 0.43 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.37 - 0.45 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.37 - 0.45 | % | ISO 2577 |
| Traffic : 3.20mm | 0.35 - 0.43 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 116 | ASTM D785 | |
| R scale | 116 | ISO 2039-2 | |
| Pencil Hardness 1 | H | JIS K5401 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2500 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 3 | 51.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 4 | 34.0 | MPa | ASTM D638 |
| Fracture | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 5 | 25 | % | ASTM D638 |
| Fracture | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2600 | MPa | ASTM D790 |
| -- 7 | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 74.0 | MPa | ASTM D790 |
| -- 9 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 110 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 98.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 91.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 78.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 to 3.0mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Hot air dryer | 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 73.5 - 235 | MPa | |
| Back Pressure | 0.490 | MPa | |
| Screw Speed | 30 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 240°CHot Runner Valve Nozzle Temperature: 240°C |
| Note Message | |
|---|---|
| 1 . | 500g |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1603 | RTP Company | PAS | RTP |
| Shinko-Lac® ASA S359 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| VINIKA® CA70GC | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Next Nylon 66 Prime Series PG15-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Plasmer 1035BM/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |