Hostacom T20H563 0907
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aGm7w9_Hostacom-T20H563-0907.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom T20H563 is a 20% talc filled homopolymer with basic stabilisation. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 to 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 to 1.4 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Flexural Modulus - Secant | 3400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 2.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 71.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 104 | °C | ISO 306/A50 |
| CLTE - Flow (23 to 85°C) | 8.0E-5 | cm/cm/°C | DIN 53752 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 40 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT6140-01UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Sinvicomp SRP8602 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sup-tech AS103 | Shanghai Suptech Engineering Plastics Co. Ltd. | ABS+Nylon | Sup-tech |
| Nipol® LX852B | Zeon Corporation | Latex | Nipol® |
| DOMAMID® 24 | DOMO Caproleuna GmbH | Nylon 6 | DOMAMID® |