NOVAPOL® LF-0718-A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aFY3LR_NOVAPOL-LF-0718-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL®LF-0718-A is a low density polyethylene material,. This product is available in North America and is processed by film extrusion or extrusion coating. NOVAPOL®The main features of the LF-0718-A are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 125 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 140 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 19.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 14.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 470 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 170 | g | ASTM D1922 |
| TD : 38 µm, blown film | 98 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 56 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (38.0 µm) | 170 | J/cm | Internal method |
| Film properties are typical of blown film extruded on a 1.5" extruder with 3" die and 35-mil die gap at a blow up ratio of 2.5:1, but are dependent upon operating conditions. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH 731E | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Tarnamid® T-27 GF 140 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| WPP JOSB26569-Black | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP |
| KARINTOX 70/2 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | KARINTOX |
| Zytel® ST801AW NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |