LNP™ LUBRICOMP™ KP004L compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aFKO9P_LNP-LUBRICOMP-KP004L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KP004L is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant, Low Extractible. Also known as: LNP* LUBRICOMP* Compound KL-4540 LE Product reorder name: KP004L |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 2.8 to 3.0 | % | ASTM D955 |
| Across Flow : 24 hr | 2.3 to 2.5 | % | ASTM D955 |
| Across Flow : 24 hr | 2.4 | % | ISO 294-4 |
| Flow : 24 hr | 2.9 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2270 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2 |
| Break | 46.2 | MPa | ASTM D638 |
| Break | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 20 | % | ASTM D638 |
| Yield | 19 | % | ISO 527-2 |
| Break | 40 | % | ASTM D638 |
| Break | 34 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 5400 | MPa | ISO 178 |
| Flexural Stress | 119 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.27 | ||
| vs. Itself - Static | 0.15 | ||
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 3 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.00 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 151 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 81.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 88.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNISOFT TPE™ ST-65A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Altuglas® V 045 I | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Elastollan® 1185 A FHF | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Epolene® N-14P | Westlake Chemical Corporation | LDPE | Epolene® |
| Hostacom TKC 232N | LyondellBasell Industries | PP Copolymer | Hostacom |