INEOS LDPE 24W930
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aEoHTw_INEOS-LDPE-24W930.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
24W930 is a low-density polyethylene intended for injection rnoulding and compounding. It is a high MFR material, having good flow properties and allowing short cycle tirne. The moulded article is characterised by low degree of built-in stress, good stiffness and high gloss. 24W930 is recommended for injection moulding of flexible products which require good flow properties and short cycle time. The material is especially suitable for thin walled products like caps and closures, household goods and toys. It is also recommended for the manufacturing of highly filled compounds. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 55 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 4.00 mm, Compression Molded) | 47 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Compression Molded) | 260 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield, 4.00 mm, Compression Molded | 10.4 | MPa | |
| Break, 4.00 mm, Compression Molded | 8.60 | MPa | |
| Tensile Strain (Break, 4.00 mm, Compression Molded) | 100 | % | ISO 527-2 |
| Flexural Modulus (23°C, 4.00 mm, Compression Molded) | 300 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A |
| Melting Temperature (DSC) 1 | 108 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UTTAP ES 10559 | Ovation Polymers Inc. | PC Alloy | UTTAP |
| Karina GRAY PVC COMPOUND 805-18/105-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND -E 80/202-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® LLH1018A | Osterman & Company | LLDPE | Osterlene® |
| Sylvin 5132-86 Clear 8373 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |