INTEGRAL™ 602

Category:	Polyolefin, Unspecified , Polyolefin Adhesive Film
Manufacturer:	The Dow Chemical Company
Trademark:	INTEGRAL™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aDg9iW_INTEGRAL-602.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
INTEGRAL™ 602 Polyolefin Adhesive Film is a heat-activated adhesive film specifically formulated for bonded to steel on both sides of the film. It can also be used as a tie layer to bond two substrates together. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. General Characteristics: Heat Activation Point: 215 °F (102 °C) Yield: 208 ft²/lb/mil (42.6 m²/kg/25 µm) Available Colors: Green Gauge Range: 1.5-4.0 mil (38-102 µm) Width Range: 15-65 inches (380-1650 mm)

General Information
Appearance	Green
Forms	Film

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	58	µm
Film Thickness - Recommended / Available	1.5-4.0 mil (38-102 µ)
Secant Modulus			ASTM D882
1% Secant, MD : 58 µm	343	MPa
2% Secant, MD : 58 µm	266	MPa
1% Secant, TD : 58 µm	335	MPa
2% Secant, TD : 58 µm	265	MPa
Tensile Strength			ASTM D882
MD : Yield, 58 µm	14.5	MPa
TD : Yield, 58 µm	13.1	MPa
MD : Break, 58 µm	32.8	MPa
TD : Break, 58 µm	25.9	MPa
Tensile Elongation			ASTM D882
MD : Yield, 58 µm	15	%
TD : Yield, 58 µm	15	%
MD : Break, 58 µm	520	%
TD : Break, 58 µm	560	%
Elmendorf Tear Strength			ASTM D1922
MD : 58 µm	550	g
TD : 58 µm	760	g
Film Width	38.10 to 165.10	cm
Yield (25.0 µm)	42.6	m²/kg

Thermal	Nominal Value	Unit
Heat Activation Temperature	102	°C

Resin Grade	Manufacturer	Category	Trademark
Telcar® TL-2430F	Teknor Apex Company	TPE	Telcar®
SUMILITE® PL-1252 (Machining)	Sumitomo Bakelite Co., Ltd.	Phenolic	SUMILITE®
FORMULA P ELAN 5220 M2	Putsch Kunststoffe GmbH	PP, Unspecified	FORMULA P
Infino VB-5400G	SAMSUNG SDI CO., LTD.	PBT	Infino
LUVOCOM® 1106-7940/GY/EM	Lehmann & Voss & Co.	PEI	LUVOCOM®