SUPREME Specialty PS SP265

Category:	PS (Specialty) , Specialty Polystyrene
Manufacturer:	Supreme Petrochem Ltd.
Trademark:	SUPREME Specialty PS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aBFRgX_SUPREME-Specialty-PS-SP265.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Toughened Polystyrene

Characteristics:

Good Clarity

High Dart Impact Strength

High Heat Resistance

Good Stiffness

Excellent Low Temperature Toughness

Processing:

Extrusion & Forming

Applications:

Disposable glasses & bowls

Deep draw formed products

Thermoformed hot fill & frozen Food packing applications

Blended with HIPS for improved toughness & gloss

General Information
Features	Low Temperature Flexibility Rigid, good High strength Impact resistance, high Heat resistance, high Compliance of Food Exposure Disposable Medium transparency
Uses	Cup Kitchen utensils Container Food packaging
Agency Ratings	FDA 21 CFR 177.1640
Forms	Particle
Processing Method	Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.02	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	6.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(23°C, 3.20 mm, Injection Molded)	35.0	MPa	ASTM D638
Tensile Elongation ²(Break, 23°C, 3.20 mm, Injection Molded)	30	%	ASTM D638
Flexural Modulus (23°C, 3.20 mm, Injection Molded)	1800	MPa	ASTM D790
Flexural Strength (23°C, 3.20 mm, Injection Molded)	50.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.20 mm, Injection Molded)	15	J/m	ASTM D256
Unnotched Izod Impact (23°C, 3.20 mm)	300	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded)	79.0	°C	ASTM D648
Vicat Softening Temperature	101	°C	ASTM D1525 ³

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Transmittance (1000 µm)	86.0	%	ASTM D1003
Haze (1000 µm)	5.5	%	ASTM D1003

Additional Information
The value listed as Haze, ASTM D1003 may not have been tested according to this standard.The value listed as Transmittance, ASTM D1003 may not have been tested according to this standard.

Extrusion	Nominal Value	Unit
Melt Temperature	220	°C

Note Message
1 .	50 mm/min
2 .	50 mm/min
3 .	标准 B (120°C/h), 压力1 (10N)

Resin Grade	Manufacturer	Category	Trademark
NEXUS PC PCFG30	Nexus Resin Group, LLC.	PC	NEXUS PC
Ferro PP LPP35BC34BK	Ferro Corporation	PP Homopolymer	Ferro PP
LEXAN™ HF1140R resin	SABIC Innovative Plastics	PC	LEXAN™
POLYfill PPH GF20005 PD2 UV	Polykemi AB	PP Homopolymer	POLYfill
Diakon® Frost 952 60	Lucite International Holland BV	Acrylic (PMMA)	Diakon®