PermaStat® 305
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | PermaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aAHXKo_PermaStat-305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 - 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 86.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D 955, 3.175mm: 1-2mm/mTensile Elongation, ASTM D 638: 1-3%Static Decay, FTMS-4046.1, Mil B-81705C: <2.0 secondsVolume Resistivity, ASTM D 257: 1000000000 - 10000000000 ohm-cmSurface Resistivity, ASTM D 257: 10000000000 - 100000000000 ohm/sq |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 288 - 343 | °C | |
| Middle Temperature | 288 - 343 | °C | |
| Front Temperature | 288 - 343 | °C | |
| Mold Temperature | 66.0 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Flexible 7040 BLK | Prime PVC® | PVC, Flexible | Prime Flexible |
| Altuglas® BS 550 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| KRATON® D1133 K | Kraton Polymers LLC | SBS | KRATON® |
| Starex WR-9700 T | LOTTE ADVANCED MATERIALS CO., LTD. | ASA | Starex |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |