Durethan® BC 30 S 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a90Ce2_DurethanBC30S000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, injection molding |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.12 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 270°C, 2.00mm 1 | 0.90 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.30 | -- | % | ISO 294-4 |
| Flow direction : 270°C, 2.00mm 3 | 1.0 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.30 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 80.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | 24 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 2800 | 1000 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 90.0 | 30.0 | MPa | ISO 178/A |
| 23°C | 105 | 40.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | 7.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 14-030 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 25.0 | -- | J | ISO 6603-2 |
| -- 9 | 55.0 | -- | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 10 | 4400 | -- | N | ISO 6603-2 |
| -- 11 | 5000 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 200 | -- | kJ/m² | ISO 180/1U |
| 23°C | No Break | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 172 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 66.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 12 | 221 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; WZ 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; WZ 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E885PFAB | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| GLAMIDE® NB-5550 | TOYOBO America, Inc. | Nylon, Unspecified | GLAMIDE® |
| Kpren CM435 | Shandong Xuye New Materials Co., Ltd. | CM | Kpren |
| Polygen SC6C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| 3M™ Dyneon™ Fluoroelastomer FE 5642 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |