Lupoy® GP5300
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a8QtUz_Lupoy-GP5300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy®GP5300 is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) material, and its filler is 30% glass fiber reinforced material. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.20 mm) | 111 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm) | 1.5 | % | ASTM D638 |
| Flexural Modulus 1(3.20 mm) | 7550 | MPa | ASTM D790 |
| Flexural Strength 2(3.20 mm) | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 117 | °C | ASTM D648 |
| Additional Information |
|---|
| All properties, except melt flow rate are measured on injection molulded specimens and after 48 hours storage at 23°C, 50% relative humidty. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Minimum Moisture Content | 0.020 | % | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 250 - 265 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Back Pressure | 0.0196 - 0.0588 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3671A NAT 601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 281 AR 10 | RTP Company | Nylon 66 | RTP |
| SHIN-A SER-1500 | SHIN-A T&C | Epoxy | SHIN-A |
| TOTAL Polyethylene LDPE 1070 MN 18 C | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |