Queo™ 8230 is an ethylene based octene plastomer produced in a solution polymerisation process using a metallocene catalyst.

Supplied in the form of free flowing pellets, Queo 8230 is designed to offer:

Outstanding flexibility, even at low temperatures

Outstanding toughness

High clarity

High filler acceptance

Excellent polyolefin compatibility

Applications:
Demonstrated applications include :

Impact modification of PP

Halogen free flame retardant compounds

Automotive PP compounds

Rotational moulding

Extrusion coated structures

Additives:

Queo 8230 contains processing stabilizers.

General Information
Additive	Impact Modifier Unspecified Stabilizer
Features	Flame Retardant Good Flexibility Good Toughness Halogen Free High Clarity Low Temperature Flexibility
Uses	Automotive Applications Compounding
Forms	Pellets
Processing Method	Extrusion Rotational Molding

Physical	Nominal Value	Unit	Test Method
Density	0.882	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	30	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance	> 1000	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness			ISO 868
Shore A	83
Shore D	< 30

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	7.00	MPa	ISO 527-2/5A
Tensile Strain (Break)	980	%	ISO 527-2/5A
Flexural Modulus	22.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (23°C)	No Break		ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	43.0	°C	ISO 306/A
Melting Temperature (DSC)	76.0	°C	ISO 11357

Extrusion	Nominal Value	Unit	Test Method
Draw Down	480	m/min	Internal Method
Neck-in - 100 m/min	62.0	mm	Internal Method

Resin Grade	Manufacturer	Category	Trademark
RTP 202A HI	RTP Company	Nylon 6	RTP
Visico™ LE4423/Ambicat™ LE4472	Borealis AG	XLPE	Visico™
ANYPOL SE-2000	SH Energy & Chemical	PS (EPS)	ANYPOL
ESTYRENICS 442	PCC Plastics & Consultations Center	PS (HIPS)	ESTYRENICS
Magnobond 2004	Magnolia Plastics, Inc.	Epoxy	Magnobond