Santoprene™ 123-40
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Santoprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a73GzZ_Santoprene-123-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is a hard, black, UV-resistant thermoplastic vulcanized elastomer (TPV) in the thermoplastic elastomer (TPE) series. This material has good physical properties and chemical resistance at the same time, and is suitable for a wide range of fields. This brand of Shanduping TPV is a shear rate dependent product that can be processed on conventional thermoplastic injection molding, extrusion molding, blow molding, thermoforming or vacuum forming equipment. This is a polyolefin-based material that can be recycled in the production process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.958 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shaw D, 15 seconds, 23°C, 2.00mm) | 41 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain, 23°C) | 9.10 | MPa | ASTM D412, ISO 37 |
| Tensile Strength - Across Flow (Break, 23°C) | 19.1 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation - Across Flow (Break, 23°C) | 620 | % | ASTM D412, ISO 37 |
| Tear Strength - Across Flow | |||
| 23°C 1 | 67.0 | kN/m | ASTM D624 |
| 23°C 2 | 67 | kN/m | ISO 34-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | -17 | % | ASTM D573, ISO 188 |
| Change in Ultimate Elongation in Air (150°C, 168 hr) | -22 | % | ASTM D573, ISO 188 |
| Change in Durometer Hardness in Air (support d, 150°C, 168 hr) | 2.0 | ASTM D573, ISO 188 | |
| Change in Tensile Strength (125°C, 70 hr, in IRM 903 Oil) | -27 | % | ASTM D471, ISO 1817 |
| Change in Ultimate Elongation (125°C, 70 hr, in IRM 903 Oil) | -31 | % | ASTM D471, ISO 1817 |
| Change in Volume | |||
| 125°C, 70 hr, in IRM 903 oil | 45 | % | ASTM D471 |
| 125°C, 70 hr, in IRM 903 oil | 45 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -58.0 | °C | ASTM D746, ISO 812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 2.00 mm) | 31 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1.98 mm) | 2.60 | ASTM D150, IEC 60250 |
| Additional Information |
|---|
| 如果适用，这是基于扇形浇口注塑成型的平板测试结果。拉伸强度、伸长率和拉伸应力沿垂直流动方向测定 - ISO 1 型，ASTM die C。从埃克森美孚欧洲分支机构直接购买的所有产品都符合 REACH 法规。 对于埃克森 美孚未进口至欧洲的产品，用户应自行评估其是否满足 REACH 法规。 |
| Legal statement |
|---|
| 未经埃克森美孚化工书面允许，这种产品包括其产品名称，不得在任何医疗应用领域予以使用或有关详细的产品监管信息，请联系客户服务。 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 193 | °C | |
| Middle Temperature | 199 | °C | |
| Front Temperature | 204 | °C | |
| Nozzle Temperature | 210 - 238 | °C | |
| Processing (Melt) Temp | 216 - 232 | °C | |
| Mold Temperature | 10.0 - 51.7 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent Depth | 0.025 | mm |
| Injection instructions |
|---|
| Santoprene TPV与乙缩醛和PVC不相容。更多关于加工和模具设计的信息，请查阅我们的《注射成型指南》。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 216 | °C | |
| Back Pressure | 5.00 - 20.0 | MPa |
| Extrusion instructions |
|---|
| Santoprene TPV与乙缩醛和PVC不相容。更多关于加工和模具设计的信息，请查阅我们的《挤出成型指南》。 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 900 TFE 15 | RTP Company | PSU | RTP |
| VESTAMID® Care ML16 | Evonik Industries AG | Nylon 12 | VESTAMID® Care |
| KumhoSunny ABS 790S | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| LNP™ LUBRICOMP™ UX05051 compound | SABIC Innovative Plastics Europe | PPA | LNP™ LUBRICOMP™ |
| MAJORIS AFR090 - 8229 | AD majoris | PP Copolymer | MAJORIS |