Kingfa FRHIPS-117
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a6MyID_Kingfa-FRHIPS-117.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa FRHIPS-117 is a High Impact Polystyrene material. It is available in Asia Pacific or North America. Important attributes of Kingfa FRHIPS-117 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 40 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 2000 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 34.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 75.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.00 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 HS NTLA013 NR323 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Chemlon® 60AL | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| HiFill® HDPE GF30 BK | Techmer Engineered Solutions | HDPE | HiFill® |
| Paracril® BJLT M60 | INSA | NBR | Paracril® |
| Rotuba CAB B9004 (8% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |