LNP™ THERMOCOMP™ KF005 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a5gKiA_LNP-THERMOCOMP-KF005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* KF005 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber. Added features of this material include: Chemically Coupled. Also known as: LNP* THERMOCOMP* Compound KFX-1005 Product reorder name: KF005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.28 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 12900 | MPa | ASTM D638 |
| Tensile Strength | |||
| Break 2 | 107 | MPa | ASTM D638 |
| Break | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 4.2 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 545 | MPa | ASTM D790 |
| -- 5 | 10200 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 38.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| 23°C 7 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 8 | 39 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 162 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 161 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoDur PBT 4 GF10 black (9991) | TechnoCompound GmbH | PBT | TechnoDur |
| Vydyne® R543 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| XANTAR® MX 1020 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| APEX® 85-J644Z-3 | Teknor Apex Company | PVC, Flexible | APEX® |
| FOZEAS® J9501E50 | Mitsubishi Chemical Performance Polymers, Inc. | PLA | FOZEAS® |