Isoplast® 101 ETPU
| Category: | ETPU , Engineering Thermoplastic Polyurethane |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Isoplast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a5PgZX_Isoplast-101-ETPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Type: Isoplast® 101 is an engineering thermoplastic polyurethane resin. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.17 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 48.0 | MPa | |
| Break | 48.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 160 | % | |
| Flexural Modulus | 1800 | MPa | ASTM D790 |
| Flexural Strength | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.20 mm | 160 | J/m | |
| 23°C, 3.20 mm | 1300 | J/m | |
| 23°C, 6.40 mm | 1100 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -29°C | 68.0 | J | |
| 23°C | 68.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 71.0 | °C | |
| 0.45 MPa, Annealed | 82.0 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| 1.8 MPa, Annealed | 77.0 | °C | |
| Vicat Softening Temperature | 89.0 | °C | ASTM D1525 |
| CLTE - Flow | 8.1E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Suggested Shot Size | 25 | % | |
| Rear Temperature | 205 | °C | |
| Middle Temperature | 220 | °C | |
| Front Temperature | 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Processing (Melt) Temp | 220 to 245 | °C | |
| Injection Rate | Slow | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 T30 UV NTLA010 NR434 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| EnCom F0 PBT 30 GF | EnCom, Inc. | PBT | EnCom |
| Huafon JF-S-WV7030 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| PENTAMID B GV15 GK15 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| POLYFLAM® RPP 4000 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |