Ensinger FORMPLAST® 2000
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ensinger Inc. |
| Trademark: | Ensinger |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4yM11_Ensinger-FORMPLAST-2000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FORMPLAST™ 2000 is a thermoplastic composite material with superior properties for use in thermoforming plug assist applications. FORMPLAST™ 2000 has a micro-porosity of 15-19 compared to 20-30 for Syntactic Foam. FORMPLAST™ 2000 eliminates many of the problems associated with Syntactic Foam, machined aluminum or wood to become the new material of choice for plug assists. FORMPLAST®2000 is extremely tough, dimensionally stable, and chemically resistant making it an ideal plug assist material in the thermoforming or vacuumforming process of various plastics such as: PS, PETG, HDPE, PET, ABS, PVC, HIPS, PE, K (Crystal Styrene), PP and Vinyl. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (23°C) | 1790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 68.9 | MPa | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2210 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 89.6 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 82.7 | MPa | ASTM D695 |
| Shear Strength (23°C) | 68.9 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 116 | °C | ASTM D648 |
| Vicat Softening Temperature | 144 | °C | |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1090 | J/kg/°C | |
| Thermal Conductivity | 0.32 | W/m/K |
| Additional Information |
|---|
| Data based on injection molded samples. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V972 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| AKROMID® A3 K1 FR black 950089 (2246) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Cevian®-N GRSJ3 | Daicel Polymer Ltd. | SAN | Cevian®-N |
| LUVOCOM® 1-8934/BL/L | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Polifor® 20 TR/20 UV GRIGIO 7153 | SO.F.TER. SPA | PP Homopolymer | Polifor® |