KRATON® D1161 B
| Category: | SIS , Styrene Isoprene Styrene Block Copolymer |
| Manufacturer: | Kraton Polymers LLC |
| Trademark: | KRATON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4q8yh_KRATON-D1161-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Kraton D1161 B is a clear, linear block copolymer based on styrene and isoprene with a polystyrene content of 15%. It is supplied from South America in the physical form identified below.
Kraton D1161 B is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen and polymers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 2781 |
| Apparent Density | 0.35 | g/cm³ | ASTM D1895B |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.5 to 19 | g/10 min | ISO 1133 |
| Solution Viscosity 1 | 1100 | mPa·s | Internal Method |
| Antioxidant Additive | 0.080 to 0.21 | % | Internal Method |
| Ash Content | ISO 247 | ||
| BSM | 2.5 to 5.0 | % | |
| BT | < 0.50 | % | |
| Molecular Weight | 207000 to 237000 | g/mol | Internal Method |
| Polystyrene Content | 14 to 17 | % | Internal Method |
| Total Extractables | < 1.0 | % | Internal Method |
| Volatile Matter | < 0.30 | % | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coupling Efficiency | 78 to 84 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 30 sec, Compression Molded) | 30 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(300% Strain) | 0.900 | MPa | ISO 37 |
| Tensile Stress 3(Yield) | 28.0 | MPa | ISO 37 |
| Tensile Elongation 4(Break) | 1300 | % | ISO 37 |
| Note Message | |
|---|---|
| 1 . | Measured on 25% mass solution in toluene at 25°C using a Brookfield viscometer, LTF or LTV model |
| 2 . | Measured on films cast from a solution in toluene |
| 3 . | Measured on films cast from a solution in toluene |
| 4 . | Measured on films cast from a solution in toluene |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-765B | CHI MEI CORPORATION | ABS | POLYLAC® |
| SWANCOR Epoxy 901 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Vydyne® 21X1 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Kazan LDPE 153-03K | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| TechnoGreen PP LGF 30-10-04 | TechnoCompound GmbH | PP, Unspecified | TechnoGreen |