4LAC® 10H20000 A-M
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | 4Plas |
| Trademark: | 4LAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a43aOt_4LAC-10H20000-A-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LAC 10H20000 A-M is a Prime Standard Flow Unfilled Anti-Microbial ABS |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 12 - 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.60 | % | ISO 2557 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 43.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 108 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 30 - 50 °CBack Pressure: Low |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® RE 8118 | Teknor Apex Company | PVC, Rigid | APEX® |
| Crastin® FG6129 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Daelim Po1y® LH7200 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| KumhoSunny ABS 730Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Plexiglas® V825UVA | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |