TIPELIN® FS 383-03
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a3dXpZ_TIPELIN-FS-383-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN FS 383-03 is a film grade of medium density polyethylene copolymer (with hexene-1 as comonomer) grade. The product has very good Elmendorf tear strength and Dart drop resistance. The grade contains antioxidants and acid scavenger. Applications TIPELIN FS 383-03 is recommended for bags, shopping bags, multi-layer films and blend component for LDPE. TIPELIN FS 383-03 is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.18 | g/10 min | |
| 190°C/21.6 kg | 15 | g/10 min | |
| 190°C/5.0 kg | 0.87 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Compression Molded) | 900 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 24.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 19.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 51.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 48.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 700 | % | |
| TD : Break, 70 µm, Blown Film | 800 | % | |
| Dart Drop Impact (70 µm, Blown Film) | 100 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm, Blown Film | 0.45 | N | |
| TD : 70 µm, Blown Film | 3.6 | N | |
| Spencer Impact - Blown Film (70.0 µm) | 37.0 | MPa | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time - Compression Molded (200°C) | 42 | min | EN 728 |
| Vicat Softening Temperature | 119 | °C | ISO 306/A120 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vexel B12GF45 | Custom Resins Group | PBT | Vexel |
| Unichem 6111A | Colorite Polymers | PVC, Unspecified | Unichem |
| Fusabond® M623XF | DuPont Packaging & Industrial Polymers | PE Copolymer | Fusabond® |
| LEXAN™ XHT2141 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 5145-85 Clear 8255 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |