Adsyl 7416 XCP
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a3ShGG_Adsyl-7416-XCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adsyl 7416 XCP is an advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications. This grade features a low seal initiation temperature and good optics. It does not contain slip or anti-block additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 14 | % | ISO 527-2 |
| Flexural Modulus | 600 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm | 290 | MPa | |
| TD : 50 µm, Cast Film | 320 | MPa | |
| Tensile Stress | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 15.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 15.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 40.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 42.0 | MPa | |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 19 | % | |
| TD : Yield, 50 µm, Cast Film | 12 | % | |
| MD : Break, 50 µm, Cast Film | 950 | % | |
| TD : Break, 50 µm, Cast Film | 900 | % | |
| Seal Initiation Temperature | 115 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 115 | °C | ISO 306/A50 |
| Melting Temperature | 133 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 90 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 0.50 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8328-65FUV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| BJB Polyurethane SP-82 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Fainplast PVC PK 100 | Fainplast Compounds S.r.l | PVC, Semi-Rigid | Fainplast PVC |
| Flontech® FT-CAR13-GR2-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Formolene® 5143H | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |