Daicel PP PP-AF30-K2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Daicel PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a1g1y4_Daicel-PP-PP-AF30-K2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Daicel PP PP-AF30-K2 is a Polypropylene material filled with long glass fiber. It is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 115 | MPa | ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 161 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 180 to 230 | °C | |
| Middle Temperature | 190 to 240 | °C | |
| Front Temperature | 200 to 250 | °C | |
| Nozzle Temperature | 200 to 250 | °C | |
| Mold Temperature | 30.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6411 1924 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| Desmopan® 385 E | Covestro - PUR | TPU-Polyester | Desmopan® |
| Elastron® G G400.A60.T | Elastron USA, Inc. | SEBS | Elastron® G |
| ESTABLEND 0840 GF | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| Karina CLEAR PVC COMPOUND -E 80/229-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |