Hanwha Total PP BJ500
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a1UArm_Hanwha-Total-PP-BJ500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BJ500 is a high impact block copolymer which has high ethylene-propylene rubber content. Due to optimum rubber design, BJ500 has an excellent property balance between high stiffness and impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 29.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 49 | J/m | ASTM D256 |
| 0°C | 59 | J/m | ASTM D256 |
| 20°C | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 75 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 200 | °C | |
| Middle Temperature | 180 - 210 | °C | |
| Front Temperature | 200 - 230 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Pressure | 78.5 - 118 | MPa | |
| Holding Pressure | 58.8 - 98.1 | MPa |
| Injection instructions |
|---|
| Cooling Time: 25 to 40 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3935T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TRANSMARE® 35HNF30-0.101 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| GATONE™ 5330FC | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |
| HAIPLEN EP100 K10 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Plaslube® TPX-POM-01060 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |