TECHNYL® A 216 S30 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a0p9nv_TECHNYL-A-216-S30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, reinforced with 30% of glass spheres, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.6 | -- | % | |
| Flow | 1.6 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.75 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4500 | -- | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 80.0 | -- | MPa | |
| Break | 80.0 | -- | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 4.0 | -- | % | |
| Break | 9.0 | -- | % | |
| Flexural Modulus | 3850 | -- | MPa | ISO 178 |
| Flexural Stress | 135 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 20 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 2.5 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+14 | 5.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+14 | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 26 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren N220 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Yanshan PE LD607 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Baydur® 730 IBS (35 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| INEOS PP 200-CA13 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| Luranyl® KR 2403 G6 TW 26343 | ROMIRA GmbH | PPE+PS | Luranyl® |