DOW™ Electrical & Telecommunications DFDA-1375 RD

Category:	LLDPE , Cable Jacketing Compound for Cable Identification
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ Electrical & Telecommunications
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZzmboG_DOW-Electrical-Telecommunications-DFDA-1375-RD.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
DFDA-1375 RD is a linear low density polyethylene cable sheath material, which is supplied in the form of pellets. This product is specially used for processing identifiable power cables. When the thickness is 10 mils (0.25mm), its opacity is higher than that of DFDA-1374 RD. The product has an organic pigment and filler system, which makes it have excellent color retention in acid, alkali and water. This product is compatible with LLDPE sheath and is recommended to be used as a strip with DFDG-6059 BK. Specifications DFDA-1375 RD meets the following raw material specifications: ASTM D 1248 Type 1, Class B, Category 4, Grades J1 and J3

General Information
Uses	Cable sheath Wire and cable applications
Forms	Particle
Processing Method	Profile extrusion molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.925	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.75	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (20% Igepal, F0)	> 100	hr	ASTM D1693

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	16.5	MPa	ASTM D638
Tensile Elongation (Break)	700	%	ASTM D638

Aging	Nominal Value	Unit	Test Method
Tensile strength retention rate ¹	100	%	ASTM D638
Elongation retention rate ²	100	%	ASTM D638

Additional Information	Nominal Value	Test Method
Color Retention ³		Internal method
immersion in 2.5% NaOH @ 23 & 60°C : 254.0 µm	PASS	Internal method
immersion in 5% HCl @ 23 & 60°C : 254.0 µm	PASS	Internal method
immersion in Saturated Aqueous H2S @ 23°C : 254.0 µm	PASS	Internal method
immersion in Tap Water @ 23°C & 60°C : 254.0 µm	PASS	Internal method

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature ⁴	-76.0	°C	ASTM D746

Extrusion	Nominal Value	Unit
Melt Temperature	218 - 246	°C

Extrusion instructions
DFDA-1375 RD provides excellent surface finish and outstanding output rates over a broad range of conditions. The optimum results are obtained by use of melt extrusion temperatures in the suggested range 218-246°C (425-475°F). However, specific recommendations for processing is best determined when the nature of the application and type of processing equipment are known. The local Dow Wire & Cable sales representative can be contacted for such applications.

Extrusion instructions

DFDA-1375 RD provides excellent surface finish and outstanding output rates over a broad range of conditions. The optimum results are obtained by use of melt extrusion temperatures in the suggested range 218-246°C (425-475°F). However, specific recommendations for processing is best determined when the nature of the application and type of processing equipment are known. The local Dow Wire & Cable sales representative can be contacted for such applications.

Note Message
1 .	1000 hours
2 .	1000 hours
3 .	No color change after 32 weeks
4 .	F50

Resin Grade	Manufacturer	Category	Trademark
SLOVAMID® 66 GB 40	Plastcom	Nylon 66	SLOVAMID® 66
TRIMMA® FT6125	Samyang Corporation	Acrylic (PMMA)	TRIMMA®
WPP PP M2956-002	Washington Penn Plastic Co. Inc.	PP, Unspecified	WPP PP
LUVOCOM® 1301-8305	Lehmann & Voss & Co.	PPS, Linear	LUVOCOM®
Hifax TYC 900P C11544	LyondellBasell Industries	PP Copolymer	Hifax