CYCOM® 934 is a high flow, 350°F (177°C) curing epoxy resin with good 200°F (93°C) wet and 350°F (177°C) dry service capability. CYCOM 934 is formulated for autoclave processing, but it has been successfully processed by press molding. Unidirectional tape and woven fabric impregnated with CYCOM 934 resin will retain good tack and drape for at least 10 days at 70°F (21°C). Standard cure is for two hours at 350°F (177°C). No post cure is required for 350°F (177°C) dry service capability. Recommended lay-up procedure is L-3 or L-6. Recommended cure procedure is C-5 or C-9. CYCOM 934 can be impregnated via hot melt or solution techniques on all available fibers and fabrics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity 1 | 1.30 | g/cm³ |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Modulus 2(24°C) | 4140 | MPa | |
| Tensile Strength 3(24°C) | 82.7 | MPa | |
| Tensile Elongation 4(Break) | 0.70 | % | |
| Flexural Modulus 5 | 4140 | MPa | |
| Flexural Strength 6 | 68.9 | MPa |
| Note Message | |
|---|---|
| 1 . | Neat Resin |
| 2 . | Neat Resin |
| 3 . | Neat Resin |
| 4 . | Neat Resin |
| 5 . | Neat Resin |
| 6 . | Neat Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom EP5140 A1 | Spartech Polycom | PP Homopolymer | Spartech |
| TABOND 3045 | SILON s.ro | LLDPE | TABOND |
| Kepamid® 2300VT | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| OP - PC - Filled 10GF-VO | Oxford Polymers | PC | OP - PC - Filled |
| POLIMAXX 1111NXTA8 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |