Bormed™ RD808CF-11
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zz8act_Bormed-RD808CF-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed RD808CF-11 is a random copolymer with high ethylene content. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process and blown films on tubular water quenching process as well as injection moulding and ISBM (2-stage process) for ampoules and bottles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1(23°C) | 700 | MPa | ISO 178 |
| Coefficient of Friction | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 400 | MPa | |
| TD | 400 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD | 30.0 | MPa | |
| TD | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 540 | % | |
| TD : Break | 610 | % | |
| Instrumented Puncture Test - Total Penetration Energy | 300 | J/cm | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 140 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | > 140 | ASTM D2457 | |
| Haze | < 0.50 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50% Relative Humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 1060.7 | RTP Company | PBT | RTP |
| Monprene® IN-19147 | Teknor Apex Company | TPE | Monprene® |
| Generic ABS+Acrylic | Generic | ABS+Acrylic | Generic |
| LNP™ LUBRILOY™ R2000 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| OmniLon™ PA6 GR43 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |