Trademark PE mLLD1916F
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Trademark Plastics Corporation |
| Trademark: | Trademark PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zz7NHG_Trademark-PE-mLLD1916F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trademark PE mLLD1916F is a metallocene linear low density polyethylene product,. It can be processed by coextruded film and is available in North America. The application fields of Trademark PE mLLD1916F include packaging, movies, sealing applications and food contact applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.4 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Force (25 µm) | 82.7 | N | ASTM D3763 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 165 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 181 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 13.6 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 10.3 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 52.1 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 51.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 470 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 580 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 1100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 230 | g | ASTM D1922 |
| TD : 25 µm, blown film | 500 | g | ASTM D1922 |
| Seal Initiation Temperature (25 µm, Blown Film) | 92.8 | °C | ASTM D3763 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 135 | ASTM D2457 | |
| Haze 2(25.4 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 1.5:1 or higher |
| Note Message | |
|---|---|
| 1 . | Base polymer only |
| 2 . | Base polymer only |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| Xuchuan XCW-SP20 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| YUPLENE® R366Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Hanwha Total PP RJ700 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| ICORENE® N6602 | ICO Polymers EMEA, A Division of A. Schulman | ABS | ICORENE® |